Steel Shot
Komposisi Kimia | C | 0,85-1,20% |
Si | 0,40-1,20% | |
Mn | 0,60-1,20% | |
S | ≤0,05% | |
P | ≤0,05% | |
Teu karasa | HRC 40-50 | |
Mikrostruktur | Homogén Tempered Martensite atanapi Troostite | |
Kapadetan | ≥ 7.2g/cm3 | |
Bentuk éksternal | Bulat Partikel kerung <10% |
Distribusi ukuran
Layar No. | Inci | Ukuran layar | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
6 | 0.132 | 3.35 | Kabéh lulus | |||||||||||
7 | 0.111 | 2.80 | Kabéh lulus | |||||||||||
8 | 0.0937 | 2.36 | Kabéh lulus | ≥90% | ||||||||||
10 | 0,0787 | 2.00 | Kabéh lulus | Kabéh lulus | ≥85% | ≥97% | ||||||||
12 | 0,0661 | 1.70 | Kabéh lulus | ≤5% | ≥85% | ≥97% | ||||||||
14 | 0,0555 | 1.40 | Kabéh lulus | ≤5% | ≥85% | ≥97% | ||||||||
16 | 0,0469 | 1.18 | Kabéh lulus | ≤5% | ≥85% | ≥97% | ||||||||
18 | 0,0394 | 1.00 | Kabéh lulus | ≤5% | ≥85% | ≥96% | ||||||||
20 | 0,0331 | 0.850 | Kabéh lulus | ≤10% | ≥85% | ≥96% | ||||||||
25 | 0,0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
30 | 0,0232 | 0.600 | Kabéh lulus | ≥85% | ≥96% | |||||||||
35 | 0,0197 | 0.500 | ≤10% | ≥97% | ||||||||||
40 | 0,0165 | 0.425 | Kabéh Pass | ≥85% | ||||||||||
45 | 0,0138 | 0.355 | ≤10% | ≥97% | ||||||||||
50 | 0,0117 | 0.300 | ≥80% | |||||||||||
80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
120 | 0,0049 | 0.125 | ≥90% | |||||||||||
200 | 0,0029 | 0,075 |
Aplikasi
Blast beberesih: Dipaké pikeun beberesih blast of casting, paeh-casting, forging;panyabutan keusik tina casting, plat baja, H tipe baja, struktur baja.
panyabutan karat: panyabutan karat of casting, forging, plat baja, H tipe baja, struktur baja.
Shot peening: Shot peening of gear, bagian panas diperlakukeun.
Keusik blasting: Keusik blasting tina baja profil, dewan kapal, dewan baja, bahan baja, struktur baja.
Pra-perlakuan: Pra-perlakuan permukaan, dewan baja, baja profil, struktur baja, saméméh lukisan atawa palapis.